THE INFLUENCE OF DOPING MOLYBDENUM ON THE PHYSICAL AND MECHANICAL PROPERTIES OF THE EUTECTIC ALLOY OF SYSTEM OF WC-W2C
Наукові журнали Національного Авіаційного Університету
View Archive Info| Field | Value | |
| Title |
THE INFLUENCE OF DOPING MOLYBDENUM ON THE PHYSICAL AND MECHANICAL PROPERTIES OF THE EUTECTIC ALLOY OF SYSTEM OF WC-W2C
— ВПЛИВ ЛЕГУВАННЯ МОЛІБДЕНОМ НА ФІЗИКО-МЕХАНІЧНІ ВЛАСТИВОСТІ ЕВТЕКТИЧНОГО СПЛАВУ СИСТЕМИ WC-W2C |
|
| Creator |
Троснікова, Ірина Юріївна
|
|
| Subject |
relit; sputtering; doping; durability; hardness; physical and mechanical properties
— — — реліт; розпилення; легування; зносостійкість; твердість; фізико-механічні властивості УДК 621.762 |
|
| Description |
The arrival on the market of drilling services of foreign companies has led to a change in drilling technology and substantially changed the requirements for the material and structures of drill pipes. The most demanded today are high-strength drill pipes, which occupy more than 70% of the market. The extreme conditions of operation of drill pipes lead to their destruction. The main causes of the destruction of drill pipes are cracks. They form in conditions of high loads and corrosion and abrasive wear. Assessing the statistical data, we can conclude that more than 60% of pipes are defected due to the wear of the outer diameter of the castle, while other parameters of the pipe correspond to acceptable standards. Thus, one of the priority directions in the production and overhaul of drill pipes is the surfacing with wear-resistant materials of the outer surface of the locks. The highest values of hardness and strength are achieved on materials that represent a matrix of one refractory compound reinforced with monocrystalline fibers of another refractory compound. The spherical and irregularly shaped powder particles of tungsten carbides are used for surfacing on a drilling tools. The eutectic alloy of the WC-W2C system is relit (78-80 wt. % of W2C, 20-22 wt. % of WC), which have high hardness and wear resistance. It was studied the influence of doping with molybdenum on the physical and mechanical properties of the eutectic alloy of the system WC-W2C obtained by centrifugal sputtering of the rotating electrode. It is shown that in comparison with the undoped relit, the microhardness of doped with molybdenum (5 wt. %), increases by more than 30%, durability is 2 times, and the wear resistance of spherical particles 2-3 times, which satisfactorily agrees with the change of the stress-deformed state of the phase components of composite material and is explained by the mechanism of grain boundary strengthening and deformation strengthening.
— Досліджено вплив легування молібденом на фізико-механічні властивості евтектичного сплаву системи WC-W2C, отриманого відцентровим розпиленням електроду, що обертається. Показано, що в порівнянні з нелегованим релітом мікротвердість реліту, легованого молібденом (5 % (мас.), підвищується більш ніж на 30%, міцність в 2 рази, а зносостійкість сферичних частинок у 2-3 рази, що задовільно узгоджується зі зміною напружено-деформованого стану фазових складових композиційного матеріалу і пояснюється механізмом зернограничного та деформаційного зміцнення. |
|
| Publisher |
National Aviation University
|
|
| Contributor |
—
— — |
|
| Date |
2018-09-24
|
|
| Type |
—
|
|
| Format |
application/pdf
|
|
| Identifier |
http://jrnl.nau.edu.ua/index.php/PTZ/article/view/13314
10.18372/0370-2197.3(80).13314 |
|
| Source |
Проблеми тертя та зношування; № 3(80) (2018); 56-61
Problems of Friction and Wear; № 3(80) (2018); 56-61 Проблемы трения и изнашивания; № 3(80) (2018); 56-61 |
|
| Language |
uk
|
|